In-situ pure TiO2 and Fe-doped TiO2 thin films were synthesized on Ti plates via the micro-arc oxidation (MAO) technique.The as-fabricated anatase TiO2 thin film-based conductometric sensors were employed to measure the gas sensitivity to ethanol.The results showed that Fe ions could be easily introduced into the MAO-TiO2 thin films by adding precursor K4(FeCN)6·3H2O into the Na3PO4 electrolyte.The amount of doped Fe ions increased almost linearly with the concentration of K4(FeCN)6·3H2O increasing,eventually affecting the ethanol sensing performances of TiO2 thin films.It was found that the enhanced sensor signals obtained had an optimal concentration of Fe dopant (1.28at％),by which the maximal gas sensor signal to 1000 ppm ethanol was estimated to be 7.91at 275℃.The response time was generally reduced by doped Fe ions,which could be ascribed to thc increase of oxygen vacancies caused by Fe3+ substituting for Ti4+....